Utilization of Clay and Fly Ash from Waste Industries Produced Lightweight Concrete Block for Load Bearing Wall
Keywords:
Concrete Block, Waste Industries, Pozzolanic ReactionAbstract
This research gained to using fly ash and silt from factories instead of cement, which reduced the amount of cement for production of lightweight aggregate concrete block. Calcium hydroxide (Ca(OH)2) and sodium hydroxide (NaOH) were catalysts, which added for some reactions, such as hydration, pozzolanic, and geopolymerization reaction. Ca2+, Si2+, O2-, OH- and Na2+ were increase ionization from the reactions. The formulation was 80% by weight of fly ash from paper factories and 5 molar of sodium hydroxide solution, which gained compressive strength 13.70 MPa and density 1,497 kg/m3 at 60 day of incubation. There may be available in general concrete industries.
References
ชัย จาตุรพิทักษ์กุล และ ปริญญา จินดา ประเสริฐ. (2549). ปูนซีเมนต์ ปอซ โซลาน และคอนกรีต. กรุงเทพฯ: สมาคมคอนกรีตไทย.
บุรฉัตร ฉัตรวีระ และ เพิ่มพล ศรีนวล. (2555). การศึกษาสมบัติของมอร์ ต้าร์ปอร์ตแลนด์ซีเมนต์ประเภทที่ 5 ผสมเถ้าแกลบบดและผงหินปูน. วารสารวิจัยและพัฒนา มจธ. ปีที่ 35(ฉบับที่ 2), หน้า 201 - 218.
สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. (2533). มอก 57-2533 มาตรฐาคอนกรีตบล็อกรับน้ำหนัก. กรุงเทพมหานคร . กระทรวงอุตสาหกรรม.
American society for testing and materials. (1995). “ASTM C 109/C 109M-95: Standard test method for compressive strength of hydraulic cement mortars (Using 2-in. or [50- mm.] cube Specimens)”. Annual book of ASTM standards, Vol. 04.01, pp. 68 - 72.
American society for testing and materials. (1995). “ASTM C 618- 94a: Standard specification for coal fly ash and raw or calcined natural pozzzolan for use as a meineral admixture in portland cement concrete”. Annual book of ASTM standards. Vol. 04.02, pp. 304 - 306.
Caijun S. and Robert L. D. (2000). Pozzolanic reaction in the presence of chemical activators Part II. Reaction products and mechanism. Cement and concrete research, Vol. 30, pp. 607 - 613.
Day R.L. and Shi C. (1994). Relationship between strength development of lime–natural pozzolan pastes and the blaine fineness of the natural pozzolans. Cement and concrete research, Vol. 24, pp. 1485 - 1491.
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
บทความที่ได้รับการตีพิมพ์เป็นลิขสิทธิ์ของคณะเทคโนโลยีอุตสาหกรรม มหาวิทยาลัยราชภัฎสวนสุนันทา
ข้อความที่ปรากฏในบทความแต่ละเรื่องในวารสารวิชาการเล่มนี้เป็นความคิดเห็นส่วนตัวของผู้เขียนแต่ละท่านไม่เกี่ยวข้องกับมหาวิทยาลัยราชภัฎสวนสุนันทา และคณาจารย์ท่านอื่นๆในมหาวิทยาลัยฯ แต่อย่างใด ความรับผิดชอบองค์ประกอบทั้งหมดของบทความแต่ละเรื่องเป็นของผู้เขียนแต่ละท่าน หากมีความผิดพลาดใดๆ ผู้เขียนแต่ละท่านจะรับผิดชอบบทความของตนเองแต่ผู้เดียว