Electrospun PLA/PBS/MWCNT nanocomposite fibers for high-performance air filtration: A sustainable approach
Article Sidebar
Main Article Content
Abstract
For the development of high-performance air filtration materials, electrospun polylactic acid (PLA)/polybutylene succinate (PBS) blend fibers, reinforced with multi-walled carbon nanotubes (MWCNTs), were fabricated and subjected to comprehensive characterization. A PLA/PBS blend, at a 95/5 wt% ratio, was prepared through the dissolution of the constituent polymers in a dichloromethane/dimethylformamide mixture, using a 3:1 v/v ratio at a 17 wt% concentration. MWCNTs were introduced into the polymer solution, with dispersion facilitated by a Triton X-100 surfactant and ultrasonication, at concentrations ranging from 0 to 4 wt%. Electrospinning was performed under optimized conditions, specifically an applied voltage of 16 kV and a tip-to-collector distance of 18 cm. Upon the incorporation of MWCNTs, minor alterations to fiber morphology were observed, including a slight increase in fiber diameter and an enhancement in the uniformity of surface pore distribution. Thermal properties were analyzed, revealing a trend of decreasing glass transition temperature, melting temperature, and thermal stability as the MWCNT content increased. Mechanical properties were evaluated, with improvements in tensile strength and Young's modulus documented with increasing MWCNT content. Filtration efficiency was assessed, and significant enhancements were achieved, with performance comparable to N95 masks (98-99%) recorded. Notably, a reduction in pressure drop across the filters was observed with increasing MWCNT content, indicating improved breathability. The potential of these biodegradable and environmentally sustainable nanocomposite fibers as an alternative to conventional filtration materials, addressing the growing concerns surrounding air pollution, is demonstrated by these results. This study highlights the feasibility of employing biopolymers and carbon nanomaterials for a more sustainable approach to air filtration, offering a viable solution for developing advanced, eco-friendly filtration technologies.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
References
Sangkham S, Phairuang W, Sherchan SP, Pansakun N, Munkong N, Sarndhong K, et al. An update on adverse health effects from exposure to PM2.5. Environ Adv [internet]. 2024;18:100603. Available from: https://doi.org/10.1016/j.envadv.2024.100603.
Pai SJ. Carter TS, Heald CL, Kroll JH. Updated world health organization air quality guidelines highlight the importance of non-anthropogenic PM2.5, Environ Sci Technol Lett [internet]. 2022;9(6):501-6. Available from: http://doi.org/10.1021/acs.estlett.2c00203.
Selvaranjan K, Navaratnam S. Rajeev P, Ravintherakumaran N. Environmental challenges induced by extensive use of face masks during COVID-19: A review and potential solutions. Environ Challenges [internet]. 2021;3:100039. Available from: https://doi.org/10.1016/j.envc.2021.100039.
Villarreal-Gómez LJ, Cornejo-Bravo JM, Vera-Graziano R, Grande D. Electrospinning as a powerful technique for biomedical applications: A critically selected survey. J Biomater Sci Polym Ed [internet]. 2015;27(2);157-76. Available from: https://doi.org/10.1080/09205063.2015.1116885.
Phan DN, Khan MQ, Nguyen NT, Phan TT, Ullah A, Khatri M, et al. A review on the fabrication of several carbohydrate polymers into nanofibrous structures using electrospinning for removal of metal ions and dyes. Carbohydr Polym [internet]. 2021;252:117175. Available from: https://doi.org/10.1016/j.carbpol.2020.117175.
Dai H, Liu X, Zhang C, Ma K, Zhang Y. Electrospinning polyacrylonitrile/graphene oxide/polyimide nanofibrous membranes for high-efficiency PM2.5 filtration. Sep Purif Technol [internet]. 2021;276:119243. Available from: https://doi.org/10.1016/j.seppur.2021.119243.
Liu H, Zhu Y, Zhang C, Zhou Y, Yu DG. Electrospun nanofiber as building blocks for high-performance air filter: A review, Nano Today. 2024;55:102161. Available from: https://doi.org/10.1016/j.nantod.2024.102161.
Yu Z, Fan T, Liu Y, Li L, Liu J, Yang B, et al. Efficient air filtration through advanced electrospinning techniques in nanofibrous materials: A review. Purif Technol [internet]. 2024;349;127773. Available from: https://doi.org/10.1016/j.seppur.2024.127773.
Karabulut FNH, Höfler G, Ashok Chand N, Beckermann GW. Electrospun nanofibre filtration media to protect against biological or nonbiological airborne particles. Polym [internet]. 2021;13(19):3257. Available from: https://doi.org/10.3390/polym13193257.
Wang L, Gao Y, Xiong J, Shao W, Cui C, Sun N, et al. Biodegradable and high-performance multiscale structured nanofiber membrane as mask filter media via poly(lactic acid) electrospinning. J Colloid Interface Sci [internet]. 2022;606;961-70. Available from: https://doi.org/10.1016/j.jcis.2021.08.079.
Wang Z, Zhao C, Pan Z. Porous bead-on-string poly(lactic acid) fibrous membranes for air filtration. J Colloid Interface Sci [internet]. 2015;441121-29. Available from: https://doi.org/10.1016/j.jcis.2014.11.041.
Souzandeh H, Wang Y, Netravali AN, Zhong WH. Towards sustainable and multifunctional air-filters: A review on biopolymer-based filtration materials. Polym Rev [internet]. 2019;59(4):651-86. Available from: https://doi.org/10.1080/15583724.2019.1599391.
Hamad K, Kaseem M, Ayyoob M, Joo J, Deri F. Polylactic acid blends: The future of green. Prog Polym Sci [internet]. 2018;85:83-127. Available from: https://doi.org/10.1016/j.progpolymsci.2018.07.001.
Phiriyawirut M, Sarapat K, Sirima S, Prasertchol A. Porous electrospun nanofiber from biomass-based polyester blends of polylactic acid and polybutylene succinate. OJPChem [internet]. 2019:9(1):1-15. Available from: http://doi.org/10.4236/ojpchem.2019.91001.
Stoyanova N, Paneva D, Mincheva R, Toncheva A, Manolova N, Dubois P, et al. Poly(l-lactide) and poly(butylene succinate) immiscible blends: From electrospinning to biologically active materials. Mater Sci Eng C [internet]. 2014;41:119-26. Available from: https://doi.org/10.1016/j.msec.2014.04.043.
Prahsarn C, Klinsukhon W, Padee S, Suwannamek N, Roungpaisan N, Srisawat N. Hollow segmented-pie PLA/PBS and PLA/PP bicomponent fibers: An investigation on fiber properties and splittability. J Mater Sci [internet]. 2016;51:10910–16. Available from: https://doi.org/10.1007/s10853-016-0302-0.
Ghosal K, Agatemor C, Špitálsky Z, Sabu T, Kny E. Electrospinning tissue engineering and wound dressing scaffolds from polymer-titanium dioxide nanocomposites. Chem Eng J [internet]. 2019;358:1262-78. Available from: https://doi.org/10.1016/j.cej.2018.10.117.
Canales D, Moyano D, Alvarez F, Grande-Tovar CD, Valencia-Llano CH, Peponi L, et al. Preparation and characterization of novel poly (lactic acid)/calcium oxide nanocomposites by electrospinning as a potential bone tissue scaffold. Biomater Adv [internet]. 2023;153:213578. Available from: https://doi.org/10.1016/j.bioadv.2023.213578.
Selatile MK, Ojijo V, Sadiku R, Ray SS. Development of bacterial-resistant electrospun polylactide membrane for air filtration application: Effects of reduction methods and their loadings. Polym Degrad Stab [internet]. 2020;178:109205. Available from: https://doi.org/10.1016/j.polymdegradstab.2020.109205.
Naebe M, Lin T, Staiger MP, Dai L, Wang X. Electrospun single-walled carbon nanotube/polyvinyl alcohol composite nanofibers: Structure-property relationships. Nanotechnol [internet]. 2008;19:305702. Available from: https://doi.org/10.1088/09574484/19/30/305702.
Kaur N, Kumar V, Dhakate SR. Synthesis and characterization of multiwalled CNT–PAN based composite carbon nanofibers via electrospinning. SpringerPlus [internet]. 2016;5:483. Available from: https://doi.org/10.1186/s40064-016-2051-6.
Zadeh ZE, Solouk A, Shafieian M, Nazarpak MH. Electrospun polyurethane/carbon nanotube composites with different amounts of carbon nanotubes and almost the same fiber diameter for biomedical applications. Mater Sci Eng C [internet]. 2021;118:111403. Available from: https://doi.org/10.1016/j.msec.2020.111403.
Alruwaill BM, Saeed U, Ahmad I, Al-Turaif H, Aboalkhair H, Alsaiarl AO. Development of multiwalled carbon nanotube-reinforced biodegradable polylactic acid/polybutylene succinate blend membrane. Membr [internet]. 2021;11(10):760. Available from: https://doi.org/10.3390/membranes11100760.
Tian X, Huang Y, Lu Y, Li Z, Liu L, Wang L, et al. Fabrication of an amino-modified MWCNTs grafted with chlorosulfonated PMIA nanofibrous membrane via electrospinning for efficient high-temperature dust filtration. Sep Purif Technol [internet]. 2024;336:126193. Available from: https://doi.org/10.1016/j.seppur.2023.126193.
Namsaeng J, Punyodom W, Worajittiphon P. Synergistic effect of welding electrospun fibers and MWCNT reinforcement on strength enhancement of PAN-PVC non-woven mats for water filtration. Chem Eng Sci [internet]. 2019;193:230-42. Available from: https://doi.org/10.1016/j.ces.2018.09.019.
Madenli EC, Cakmakci O. Preparation and characterization of PAN/CNT nanocomposite fiber supports for membrane filtration. Desalination Water Treat [internet]. 2017;60:137-43. Available from: https://doi.org/10.5004/dwt.2017.0808.
Ghorabi S, Rajabi L, Madaeni SS, Zinadini S, Derakhshan AA. Effects of three surfactant types of anionic, cationic and non-ionic on tensile properties and fracture surface morphology of epoxy/MWCNT nanocomposites. Iran Polym J [internet]. 2012;21:121–30. Available from: https://doi.org/10.1007/s13726-011-0013-y.
Elsharif AM, Bukhari OA. Carbon nanofilms blended with polyvinyl pyrrolidone and Triton X-100 for energy harvesting application. Orient J Chem [internet]. 2020;36(3). Available from: http://dx.doi.org/10.13005/ojc/360306.
Pathak R, Punetha VD, Bhatt S, Punetha M. Carbon nanotube-based biocompatible polymer nanocomposites as an emerging tool for biomedical applications. Eur Polym J [internet]. 2023;196:112257. Available from: https://doi.org/10.1016/j.eurpolymj.2023.112257.
Khan W, Sharma R, Saini P. Carbon nanotube-based polymer composites: Synthesis, properties and applications. Carbon Nanotubes - Current Progress of their Polymer Composites [internet]. 2016; Available from: http://doi.org/10.5772/62497.
Lee JKY, Chen N, Peng S, L Li, Tian L, Thakor N, et al. Polymer-based composites by electrospinning: Preparation & functionalization with nanocarbons. Prog Polym Sci [internet]. 2018;86:40-84. Available from: https://doi.org/10.1016/j.progpolymsci.2018.07.002.
Mit-uppatham C, Nithitanakul M, Supaphol, P. Ultrafine electrospun polyamide-6 fibers: Effect of solution conditions on morphology and average fiber diameter. Macromol Chem Phys [internet]. 2004;205:2327-38. Available from: https://doi.org/10.1002/macp.200400225.
Xin BJ, Chen W. Morphology, structure and properties of electrospun multi-walled carbon nanotube/polysulfonamide composite nanofibers. J Eng Fibers Fabr [internet]. 2015;10(1). Available from: http://doi.org/10.1177/155892501501000105.
Chaiwutthinan P, Pimpan V, Chuayjuljit S, Leejarkpai T. Biodegradable plastics prepared from poly(lactic acid), poly(butylene succinate) and microcrystalline cellulose extracted from waste-cotton fabric with a chain extender. J Polym Environ [internet]. 2015;23:114-25. Available from: https://doi.org/10.1007/s10924-014-0689-0.
Nie P, Min C, Song HJ, Chen X, Zhang Z, Zhao K. Preparation and tribological properties of polyimide/carboxyl-functionalized multi-walled carbon nanotube nanocomposite films under seawater lubrication. Tribol Lett [internet]. 2015;58:7. Available from: https://doi.org/10.1007/s11249-015-0476-7.
Yuen SM, Ma CCM, Chiang CL, Teng CC. Morphology and properties of aminosilane grafted MWCNT/polyimide nanocomposites. J Nanomater [internet]. 2008;786405. Available from: https://doi.org/10.1155/2008/786405.
Chow WS, Lim YT. Antistatic and thermal properties of poly(lactic acid)/polypropylene/carbon nanotube nanocomposites. J Eng Sci [internet]. 2020;16(2):57-69. Available from: http://doi.org/10.21315/jes2020.16.2.3.
Ceregatti T, Pecharki P, Pachekoski WM, Becker D, Dalmolin C. Electrical and thermal properties of PLA/CNT composite films. Rev Mater [internet]. 2017;22(3). Available from: http://doi.org/10.1590/S1517-707620170003.0197.
Ghane N, Mazinani S, Gharehaghaji A. Comparing the performance of electrospun and cast nanocomposite film of polyamide-6 reinforced with multi-wall carbon nanotubes. J Plast Film Sheeting [internet]. 2019;35(1):45-64. Available from: https://doi.org/10.1177/8756087918794229.
Vorawongsagul S, Pratumpong P, Pechyen C. Preparation and foaming behavior of poly (lactic acid)/poly (butylene succinate)/cellulose fiber composite for hot cups packaging application. Food Packag Shelf Life [internet]. 2021;27:100608. Available from: https://doi.org/10.1016/j.fpsl.2020.100608.
Eun JH, Sung SM, Kim MS, Choi BK, Lee JS. Effect of MWCNT content on the mechanical and piezoelectric properties of PVDF nanofibers. Mater Des [internet]. 2021;206:109785. Available from: https://doi.org/10.1016/j.matdes.2021.109785.
Islam MS, Ashaduzzaman M, Masum SM, Yeum JH. Mechanical and electrical properties: Electrospun alginate/carbon nanotube composite nanofiber. Dhaka Univ J Biol Sci [internet]. 2012;60(1):125-28. Available from: https://doi.org/10.3329/dujs.v60i1.10350
Xiao Y, Sakib N, Yue Z, Wang Y, Cheng S, You J, et al. Study on the relationship between structure parameters and filtration performance of polypropylene meltblown nonwovens. AUTEX Res J [internet]. 2020;20(4):366-71. Available from: https://doi.org/10.2478/aut-2019-0029.