The Effect of Ammonium Sulphate on Fire Retardancy and Thermal Decomposition Mechanism of Rubberwood by LOI and TGA/DTG

Main Article Content

arphaphon chanpirak


The objective of this research was to investigate the effect of ammonium sulphate (AS) contents having concentration of 0-30 %wt impregnated on rubberwood. For this purpose, thermal degradation mechanism of samples was characterized by thermogravimetric analysis under air whereas the flammability test was applied using limiting oxygen index (LOI) and, reachability was carried out according to JIS K 1571. From TGA/DTG, the impregnation of rubberwood with AS was able to shift the decomposition temperature to the lower side temperature (215 ⁰C) and reduced the degradation rate from 11.48 to 5.45 % ºC-1, and the decomposition range of modified wood was wider than unmodified wood. The concentration levels of AS fire-retardant agent affect to change the degradation reaction of wood as a positive effect in term of a high residual weight, a low weight loss, a low initial temperature. The weight residue at 600 ⁰C are found to increase from 0.82 to 3.23 %. Especially, The LOI values of all impregnated samples with AS are classified as self-extinguishing rubberwood, and LOI increased from 26 to 42. This is indicated that the AS impregnation improves the fire retardant property of rubberwood. In addition, the leaching of AS from samples was in range 3-4 % indicated that the good fixation of AS in wood structure. Consequently, rubberwood impregnated with AS can be used as a material where fire retardancy is required.

Article Details

How to Cite
chanpirak, arphaphon. (2018). The Effect of Ammonium Sulphate on Fire Retardancy and Thermal Decomposition Mechanism of Rubberwood by LOI and TGA/DTG. Naresuan University Engineering Journal, 13(2), 1–9. Retrieved from
Research Paper


Shigematsu, A., Mizoue, N., Kajisa, T., & Yoshida, S. (2011). Importance of rubberwood in wood export of Malaysia and Thailand. New Forests, 41(2), 179–189.

Ratnasingam, J., Ioras, F., & Wenming, L. (2011). Sustainability of the rubberwood sector in Malaysia. Notulae Botanicae Horti Agrobotanici Cluj-Napoca, 39(2), 305–311.

Lee, H. L., Chen, G. C., & Rowell, R. M. (2004). Thermal properties of wood reacted with a phosphorus Pentoxide–Amine system. Journal of Applied Polymer Science, 91, 2465–2481.

Fernandes, V. J., Fernandes, N. S., Fonseca, V. M., Araujo, A. S., & Silva, D. R. (2002). Kinetic evaluation of decabromodiphenil oxide as a flame retardant for unsaturated polyester. Thermochimica Acta, 388(1–2), 283–288.

Mostashari, S. M., & Mostashari, S. Z. (2008). Combustion pathway of cotton fabrics treated by ammonium sulfate as a flame-retardant studied by TG. Journal of Thermal Analysis and Calorimetry, 91(2), 437–441.

Cheng, D., Gu, J., Xu, B., & Li, Y. (2015). Properties of Rayon Fiber from Bamboo, 10(4), 8352–8363.

Di Blasi, C., Branca, C., & Galgano, A. (2008). Thermal and catalytic decomposition of wood impregnated with sulfur- and phosphorus-containing ammonium salts. Polymer Degradation and Stability, 93(2), 335–346.

Griffin, G. J. (2011). The effect of fire retardants on combustion and pyrolysis of sugar-cane bagasse. Bioresource Technology, 102(17), 8199–8204.

Statheropoulos, M., & Kyriakou, S. A. (2000). Quantitative thermogravimetric-mass spectrometric analysis for monitoring the effects of fire retardants on cellulose pyrolysis. Analytica Chimica Acta, 409(1–2), 203–214.

Pappa, A., Mikedi, K., Tzamtzis, N., & Statheropoulos, M. (2006). TG-MS analysis for studying the effects of fire retardant on the pyrolysis of Pine-needles and their components. Journal of Thermal Analysis and Calorimetry, 84(3), 655–661.

Chen, M., Xu, L., Tian, H., Yin, C., Zhou, Z., Li, Y., … Zhong, F. (2014). Effects of common ammonium salt on the thermal behavior of reconstituted tobacco sheet. Journal of Thermal Analysis and Calorimetry, 118(3), 1747–1753.

Pérez, J., Pérez, E., del Vas, B., García, L., & Serrano, J. L. (2006). Analysis of (NH4)2SO4/ (NH4)H2PO4 mixtures by thermogravimetry and X-ray diffraction. Thermochimica Acta, 443. 231–234.

Schmidt, C. G., & Furlong, E. B. (2012). Effect of particle size and ammonium sulfate concentration on rice bran fermentation with the fungus Rhizopus oryzae. Bioresource Technology, 123, 36–41.

Wu, Z. J., Nowak, A., Poulain, L., Herrmann, H., & Wiedensohler, A. (2011). Hygroscopic behavior of atmospherically relevant water-soluble carboxylic salts and their influence on the water uptake of ammonium sulfate. Atmospheric Chemistry and Physics, 11(24), 12617–12626.

Lowden, L., & Hull, T. (2013). Flammability behaviour of wood and a review of the methods for its reduction. Fire Science Reviews, 2(1), 4.

Liodakis, S., Bakirtzis, D., & Vorissis, D. (2003). Autoignition and thermogravimetry on forest species treated with fire retardants. Thermochimica Acta, 399, 31–42.

Grexa, O., & Lübke, H. (2001). Flammability parameters of wood tested on a cone calorimeter. Polymer Degradation and Stability, 74(3), 427–432.

Liodakis, S., Kakardakis, T., Tzortzakou, S., & Tsapara, V. (2008). How to measure the particle ignitability of forest species by TG and LOI. Thermochimica Acta, 477(1–2), 16–20.

Tomak, E. D., Baysal, E., & Peker, H. (2012). The effect of some wood preservatives on the thermal degradation of Scots pine. Thermochimica Acta, 547, 76–82.

Mouritz, A. P., & Gibson, A. G. (2006). Fire properties of polymer composite materials. Dordrecht, Netherlands: Springer.

White, R. H. (1978). Oxygen Index Evaluation Of Fire-Retardant-Treated Wood. Wood Science, 12(12), 113–122.

Donmez Cavdar, A. (2014). Effect of various wood preservatives on limiting oxygen index levels of fir wood. Measurement: Journal of the International Measurement Confederation, 50(1), 279–284.

Tomak, E. D., & Cavdar, A. D. (2013). Limited oxygen index levels of impregnated Scots pine wood. Thermochimica Acta, 573, 181–185.

Gao, M., Sun, C. Y., & Wang, C. X. (2006). Thermal degradation of wood treated with flame retardants. Journal of Thermal Analysis and Calorimetry, 85(3), 765–769.

Mattos, B., Serrano, L., Gatto, D., Magalhães, W. L. E., & Labidi, J. (2014). Thermochemical and hygroscopicity properties of pinewood treated by in situ copolymerisation with methacrylate monomers. Thermochimica Acta, 596, 70–78.

Kartal, S. N., Yoshimura, T., & Imamura, Y. (2009). Modification of wood with Si compounds to limit boron leaching from treated wood and to increase termite and decay resistance. International Biodeterioration and Biodegradation, 63(2), 187–190.

Lin, L. D., Chen, Y. F., Wang, S. Y., & Tsai, M. J. (2009). Leachability, metal corrosion, and termite resistance of wood treated with copper-based preservative. International Biodeterioration and Biodegradation, 63(4), 533–538.

Venås, T. M., & Rinnan, Å. (2008). Determination of weight percent gain in solid wood modified with in situ cured furfuryl alcohol by near-infrared reflectance spectroscopy. Chemometrics and Intelligent Laboratory Systems, 92(2), 125–130.

Jiang, J., Li, J., & Gao, Q. (2015). Effect of flame retardant treatment on dimensional stability and thermal degradation of wood. Construction and Building Materials, 75, 74–81.

Liodakis, S., Antonopoulos, I., & Tsapara, V. (2009). Forest fire retardancy evaluation of carbonate minerals using DTG and LOI. Journal of Thermal Analysis and Calorimetry, 96(1), 203–209.

Liodakis, S., Tsapara, V., Agiovlasitis, I. P., & Vorisis, D. (2013). Thermal analysis of Pinus sylvestris L. wood samples treated with a new gel-mineral mixture of short- and long-term fire retardants. Thermochimica Acta, 568(September), 156–160.

Karastergiou, P. S., & Philippou, J. L. (2000). Thermogravimetric analysis of fire retardant treated particleboards. Wood and Fire Safety, 385–394.

Younis, A. A. (2016). Evaluation of the flammability and thermal properties of a new flame retardant coating applied on polyester fabric. Egyptian Journal of Petroleum, 25(2), 161–169.

Mercemik, H. (2010). Effect of Chemicals and Binders on the Durability of Flame Retardant Treated Cotton Nonwovens (Master thesis).