Increasing of Stretch Formability on Hole-flanging Parts of Aluminum Alloys by Smooth Sheared Surface
Article Sidebar
Main Article Content
บทคัดย่อ
Aluminum alloy is a lightweight material that fractures often occur during stretch forming, especially in the hole-flanging parts. However, the stretch formability of aluminum alloy increased by improving a smooth-sheared surface. The resistance of materials to edge fracture in complex shape forming is typically measured using the hole expansion ratio (HER). This paper presents the concave piercing punch design to increase smooth sheared surface which induces the increasing stretch formability of aluminum alloy. The effect of a smooth-sheared surface on stretch formability was examined via a hole expansion test (HET). The aluminum alloy grade AA1100, and AA5052 of 1.2 mm of thickness with three levels of clearance 5%t, 10%t, and 15%t were used in the experiments. The HER of aluminum alloy is influenced by a smooth sheared surface from conventional and concave piercing punch with varied clearances. In the experimental aspect, the clearance level and shape of the piercing punch, which are factors for the stretch formability of aluminum alloy, were observed by hole HER. The concave piercing punch design improves the hole expansion ratio more than a conventional piercing because a smooth sheared surface around the hole edge increases the hole expansion ratio.
Article Details
อนุญาตภายใต้เงื่อนไข Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
นโยบายการรับบทความ
กองบรรณาธิการวารสารสถาบันเทคโนโลยีไทย-ญี่ปุ่น มีความยินดีรับบทความจากอาจารย์ประจำ และผู้ทรงคุณวุฒิในสาขาวิศวกรรมศาสตร์และเทคโนโลยี ที่เขียนเป็นภาษาไทยหรือภาษาอังกฤษ ซึ่งผลงานวิชาการที่ส่งมาขอตีพิมพ์ต้องไม่เคยเผยแพร่ในสิ่งพิมพ์อื่นใดมาก่อน และต้องไม่อยู่ในระหว่างการพิจารณาของวารสารอื่นที่นำส่ง ดังนั้นผู้สนใจที่จะร่วมเผยแพร่ผลงานและความรู้ที่ศึกษามาสามารถนำส่งบทความได้ที่กองบรรณาธิการเพื่อเสนอต่อคณะกรรมการกลั่นกรองบทความพิจารณาจัดพิมพ์ในวารสารต่อไป ทั้งนี้บทความที่สามารถเผยแพร่ได้ประกอบด้วยบทความวิจัย ผู้สนใจสามารถศึกษาและจัดเตรียมบทความจากคำแนะนำสำหรับผู้เขียนบทความ
การละเมิดลิขสิทธิ์ถือเป็นความรับผิดชอบของผู้ส่งบทความโดยตรง บทความที่ได้รับการตีพิมพ์ต้องผ่านการพิจารณากลั่นกรองคุณภาพจากผู้ทรงคุณวุฒิและได้รับความเห็นชอบจากกองบรรณาธิการ
ข้อความที่ปรากฏภายในบทความของแต่ละบทความที่ตีพิมพ์ในวารสารวิชาการเล่มนี้ เป็น ความคิดเห็นส่วนตัวของผู้เขียนแต่ละท่าน ไม่เกี่ยวข้องกับสถาบันเทคโนโลยีไทย-ญี่ปุ่น และคณาจารย์ท่านอื่น ๆ ในสถาบัน แต่อย่างใด ความรับผิดชอบด้านเนื้อหาและการตรวจร่างบทความแต่ละบทความเป็นของผู้เขียนแต่ละท่าน หากมีความผิดพลาดใด ๆ ผู้เขียนแต่ละท่านจะต้องรับผิดชอบบทความของตนเองแต่ผู้เดียว
กองบรรณาธิการขอสงวนสิทธิ์มิให้นำเนื้อหา ทัศนะ หรือข้อคิดเห็นใด ๆ ของบทความในวารสารสถาบันเทคโนโลยีไทย-ญี่ปุ่น ไปเผยแพร่ก่อนได้รับอนุญาตจากผู้นิพนธ์ อย่างเป็นลายลักษณ์อักษร ผลงานที่ได้รับการตีพิมพ์ถือเป็นลิขสิทธิ์ของวารสารสถาบันเทคโนโลยีไทย-ญี่ปุ่น
ผู้ประสงค์จะส่งบทความเพื่อตีพิมพ์ในวารสารวิชาการ สถาบันเทคโนโลยีไทย-ญี่ปุ่น สามารถส่ง Online ที่ https://www.tci-thaijo.org/index.php/TNIJournal/ โปรดสมัครสมาชิก (Register) โดยกรอกรายละเอียดให้ครบถ้วนหากต้องการสอบถามข้อมูลเพิ่มเติมที่
- กองบรรณาธิการ วารสารสถาบันเทคโนโลยีไทย-ญี่ปุ่น
- ฝ่ายวิจัยและนวัตกรรม สถาบันเทคโนโลยีไทย-ญี่ปุ่น
เลขที่ 1771/1 สถาบันเทคโนโลยีไทย-ญี่ปุ่น ซอยพัฒนาการ 37-39 ถนนพัฒนาการ แขวงสวนหลวง เขตสวนหลวง กรุงเทพมหานคร 10250 ติดต่อกับคุณพิมพ์รต พิพัฒนกุล (02) 763-2752 , คุณจุฑามาศ ประสพสันติ์ (02) 763-2600 Ext. 2402 Fax. (02) 763-2754 หรือ E-mail: JEDT@tni.ac.th
เอกสารอ้างอิง
G. Fang, P. Zeng, and L. Lou, “Finite element simulation of the effect of clearance on the forming quality in the blanking process,” J. Mater. Process. Technol., vol. 122, no. 2–3, pp. 249–254, Mar. 2002.
K. Mori, Y. Abe, and Y. Suzui, “Improvement of stretch flangeability of ultra high strength steel sheet by smoothing of sheared edge,” J. Mater. Process. Technol., vol. 210, no. 4, pp. 653–659, Mar. 2010.
Z. Zhou et al., “Electromagnetic cold-expansion process for circular holes in aluminum alloy sheets,” J. Mater. Process. Technol., vol. 248, pp. 49–55, Oct. 2017.
H.-S. Choi, B.-M. Kim, and D.-C. Ko “Effect of clearance and inclined angle on sheared edge and tool failure in trimming of DP980 sheet,” J. Mech. Sci. Technol., vol. 28, no. 6, pp. 2319–2328, 2014.
Z. Tekiner, M. Nalbant, and H. Gürün, “An experimental study for the effect of different clearances on burr, smooth-sheared and blanking force on aluminium sheet metal,” Mater. Des., vol. 27, no. 10, pp. 1134–1138, 2006.
M. Sasada and T. Togashi, “Measurement of rollover in double-sided shearing using image processing and influence of clearance,” Procedia Eng., vol. 81, pp. 1139–1144, 2014.
A. A. Kamarul Adnan, S. N. Azinee, N. Norsilawati, and K. A. M. Izzul, “Analysis of the influence of the blanking clearance size to the burr development on the sheet of mild steel, brass and aluminium in blanking process,” J. Achiev. Mater. Manuf. Eng., vol. 111, no. 1, pp. 26–32, Mar. 2022.
K. Lawanwong and P. Leetrakul, “FE simulations and experimental analysis of the blade angle effect on sheared surface in trimming process of advanced high-strength steel sheet,” Arab. J. Sci. Eng., vol. 44, pp. 7909–7918, 2019.
C. Won, W. Lee, H. Lee, Y. Kang, and J. Yoon, “Effect of two-stage press blanking on edge stretchability with third-generation advanced high-strength steels,” Int J. Adv. Manuf. Technol., vol. 110, pp. 13–27, Aug. 2020.
S. Park et al., “A dual-scale FE simulation of hole expansion test considering pre-damage from punching process,” Int. J. Solids Struct., vol. 236–237, Feb. 2022, Art. no. 111312.
K. Prasad, A. S. Ebrahim, H. Krishnaswamy, U. Chakkingal, and D. K. Banerjee, “Evaluation of hole expansion formability of high strength AA7075 alloy under varying temper conditions,” IOP Conf. Ser.: Mater. Sci. Eng., 2022, Art. no. 012038, doi: 10.1088/1757-899X/1238/1/012038.
B. M. Hance, R. J. Comstock, and D. K. Scherrer, “The influence of edge preparation method on the hole expansion performance of automotive sheet steels,” SAE Tech. Paper, 2013, doi: 10.4271/2013-01-1167.
S. K. Paul, “Fundamental aspect of stretch-flangeability of sheet metals,” Proc. Inst. Mech. Eng. B, vol. 233, no. 10, 2019, doi: 10.1177/0954405418815370.
A. Karelova, C. Krempaszky, E. Werner, P. Tsipouridis, T. Hebesberger, and A. Pichler, “Hole expansion of dual-phase and complex-phase AHS steels – effect of edge conditions,” Steel. Res. Int., vol. 80, no. 1, pp. 71–77, Jan. 2009.
D. J. Branagan, A. E. Frerichs, B. E. Meacham, S. Cheng, and A. V. Sergueeva, “New mechanisms governing local formability in 3rd generation AHSS,” SAE Tech. Paper, 2017, doi: 10.4271/2017-01-1704.
Metallic materials — Method of hole expanding test, ISO/TS 16630:2009, 2009.